Engineered from a combination of Aramid Fiber and Nitrille Binder.
Applications and Characteristics:
NON ASBESTOS GASKET
Non-asbestos sheet gasket materials use synthetic fibers like aramid or Kevlar® in conjunction with an elastomeric binder.
Contact our customer services at:
+62 21 29847235
marketing@fleksindo.co.id
| Creep Relaxation | ASTM F-38B (1/32″) | 20% |
| DIN 52913 (50 MPa @ 175°C) | 28 MPa | |
| Residual Stress | BS7531 (40 MPa @ 300°C) | 20 MPa |
| Sealability | ASTM F-37A (1/32″) | 0.25 ml/hr |
| Gas Leakage | DIN 3535/6 | < 1.0 ml/min |
| Compressibility | ASTM F-36 J | 7 – 17% |
| Recovery | ASTM F-36 J | 50% min |
| Tensile Strength | ASTM F-152 | 1500 psi (10 MPa) |
| Weight Increase | ASTM F-146 after immersion in Fuel B for 5 Hrs @ 73°F (23°C) – 25% max | |
| Thickness Increase | ASTM F-146 | |
| ASTM Oil 1, 5 hrs / 300°F (149°C) | 0 – 5% | |
| ASTM Oil 3, 5 hrs / 300°F (149°C) | 0 – 5% | |
| ASTM Fuel A, 5 Hrs / 73°F (23°C) | 0 – 7% | |
| ASTM Fuel B, 5 Hrs / 73°F (23°C) | 0 – 7% | |
| Standard Line Callout | ASTM F-104 | F712121B3E22M5 |
| m & y values | 1/16″ thickness | 1/8″ thickness |
| m | 2.5 | 3.2 |
| y | 3800 | 4100 |
| Dielectric Strength | ASTM D149-95a | 15 kV/mm |
| Leachable Chlorides | FSA Method (Typical) | 100 ppm |
| Density | 112 lbs/ft³ (1.8 g/cc) | |
| Color | Blue | |
| Thickness Range | 1/64″ (0.4 mm) to 1/8″ (3.2 mm) | |
| Sheet Size Availability | Max: 120″ x 60″ (3 m x 1.5 m) | |
| Temperature Limits | -100°F to 707°F (-73°C to 375°C) | |
| Maximum Pressure | 60 Bar (870 PSI) | |