Combination between Hollow Glass Microsphere and PTFE.
Hollow Glass Microsphere. Lightweight and resistant to high temperatures.
PTFE. Resistant to various type of chemical media.
The combination of these two materials results in a PTFE gasket that is resistant to all chemical compounds and can be applied to flanges with limited torque requirements.
Contact our customer services at:
+62 21 29847235
marketing@fleksindo.co.id
| Style | Matrix 1100 | Matrix 1104 | Matrix 1110 |
|---|---|---|---|
| Color | Tan | Blue | Off White |
| Density | 137 lbs/ft³ (2.2 g/cc) | 87 lbs/ft³ (1.4 g/cc) | 180 lbs/ft³ (2.9 g/cc) |
| Temperature Limits | -450°F (-268°C) to 500°F (260°C) | -450°F (-268°C) to 500°F (260°C) | -450°F (-268°C) to 500°F (260°C) |
| MAX Pressure | 1235 psi (8.5 MPa) | 1235 psi (8.5 MPa) | 1235 psi (8.5 MPa) |
| F36 Compression | 7% | 35% | 6% |
| F36 Recovery | 45% | 45% | 40% |
| F152 Tensile Strength | 2320 psi (16 MPa) | 1885 psi (13 MPa) | 2030 psi (14 MPa) |
| F37 Liquid Leakage | <0.3 mL/hr | <0.25 mL/hr | <0.2 mL/hr |
| F38 Creep Relaxation | 35% | 31% | 13% |
| F149 Dielectric Strength | 20 kV/mm | 15 kV/mm | 21 kV/mm |
| Residual Stress BS7531 @ 175°C | 4496 psi (31 MPa) | 4351 psi (30 MPa) | 4351 psi (30 MPa) |
| Gas Leakage – DIN 3535 | <0.01 mg/(s-m) | <0.02 mg/(s-m) | <0.01 mg/(s-m) |
| Gas Leakage – BS7531 | <0.005 mL/min | <0.01 mL/min | <0.004 mL/min |
| ROTT Constant Gb | 172 | 100 | 146 |
| ROTT Constant a | 0.401 | 0.401 | 0.375 |
| ROTT Constant Gs | 2.76 x 10-6 | 2.87 x 10-5 | 1.2 |
| Tpmax | 24260 | 33240 | 60460 |
| m | 4 | 2 | 2 |
| y | 2175 psi (15 MPa) | 1595 psi (11 MPa) | 1740 psi (12 MPa) |